Adsorption and corrosion inhibition characteristics of 2–(chloromethyl) benzimidazole for C1018 carbon steel in a typical sweet corrosion environment: Effect of chloride ion concentration and temperature

Solomon, Moses M. and Onyeachu, Ikenna B. and Njoku, Demian I. and Nwanonenyi, Simeon C. and Oguzie, Emeka E. (2021) Adsorption and corrosion inhibition characteristics of 2–(chloromethyl) benzimidazole for C1018 carbon steel in a typical sweet corrosion environment: Effect of chloride ion concentration and temperature. Colloids and Surfaces A: Physicochemical and Engineering Aspects, 610.

PDF Download (8MB)

Abstract

Benzimidazole derivatives are emerging as promising corrosion inhibitors for oil and gas application because they exhibit high efficiency and very good environmental profile. Although long alkyl and phenyl chains enhance their efficiency, they also increase their toxicity. Finding benzimidazole derivatives devoid of long hydrocarbon chains and with lower toxicity has become a priority. 2–(chloromethyl)benzimidazole (CMB), with log Po/w = 2.2, has been investigated as a promising low-toxic sweet corrosion inhibitor for C1018 carbon steel in CO2–saturated NaCl solution under static condition using experimental and theoretical approaches. At 25 ◦C, Open circuit potential (OCP), electrochemical impedance spectroscopy (EIS), and potentiodynamic polarization (PDP) techniques confirm that CMB is an anodic-type sweet corrosion inhibitor which is able to form a protective layer on the steel surface and provide inhibition efficiency of 97.54% at 10 ppm. The efficiency increased to 98.40% and 98.58% upon increasing the temperature to 40 ◦C and 60 ◦C, respectively but decreased to 96.32% and 94.76% as the salt concentration was raised to 5.0% and 7.0% NaCl, respectively. The latter was attributed to the antagonistic competition between Cl– ions and CMB for anodic adsorption. The CMB–steel interaction is facilitated by the free electrons around N heteroatoms and C = C bonds, based on FTIR analysis and computational calculations. This eventually ameliorates the surface degradation of the steel during the sweet corrosion at 25 and 60 ◦C. CMB performance is highly comparable with reported sweet corrosion inhibitors with higher toxicity values.

Item Type:	Article
Uncontrolled Keywords:	Sweet corrosion Benzimidazole Corrosion inhibition Toxicity Temperature Carbon steel
Subjects:	Q Science > QD Chemistry
Divisions:	Faculty of Engineering, Science and Mathematics > School of Chemistry
Depositing User:	nwokealisi
Date Deposited:	17 Apr 2023 13:37
Last Modified:	17 Apr 2023 13:37
URI:	http://eprints.covenantuniversity.edu.ng/id/eprint/16810

Actions (login required)

View Item