Ezekiel, Somina N. and Ayoola, A. A. and Durodola, B. and Odunlami, O. A. and Olawepo, A.V (2022) Data on zinc phosphating of mild steel and its behaviour. Chemical Data Collections, 38.
![[img]](http://eprints.covenantuniversity.edu.ng/style/images/fileicons/application_pdf.png) |
PDF
Download (4MB) |
Abstract
Surface coating of A36 mild steel using zinc phosphating method was considered in this research work. The mild steel was immersed in zinc phosphating bath which was enhanced with calcium nanoparticles (obtained from snail shells and chicken eggshells). Data on zinc phosphating of the mild steel at different coating time (50 & 60 min) and coating temperatures (60 & 80 ◦C) was generated. To test the adhesion level of zinc on the mild steel, the coated mild steel was subjected to corrosion tests. And data on weight loss, corrosion rate and inhibition efficiency was generated. Surface morphology of the samples subjected to coating was determined through SEM analysis using SEM (JOEL-JSM 7600F).
| Item Type: | Article |
|---|---|
| Uncontrolled Keywords: | Calcium nanoparticles Corrosion Mild steel Surface coating Zinc phosphating |
| Subjects: | T Technology > TP Chemical technology |
| Divisions: | Faculty of Engineering, Science and Mathematics > School of Engineering Sciences |
| Depositing User: | Patricia Nwokealisi |
| Date Deposited: | 03 Mar 2025 15:14 |
| Last Modified: | 03 Mar 2025 15:14 |
| URI: | http://eprints.covenantuniversity.edu.ng/id/eprint/18845 |
Actions (login required)
 |
View Item |