Study of the corrosion behaviour of S32101 duplexand 410 martensitic stainless steel for applicationin oil refinery distillation systems

Loto, R. T. (2016) Study of the corrosion behaviour of S32101 duplexand 410 martensitic stainless steel for applicationin oil refinery distillation systems. Journal of Materials Research and Technology.

[img] PDF
Download (1MB)
Official URL: http://www.jmrt.com.

Abstract

The corrosion behaviour of S32101 duplex and 410 martensitic stainless steel was studiedthrough weight loss and potentiodynamic polarization in 1–6 M HCl solutions. Results showthat S32101 steel has significantly lower corrosion rates than 410 steel from both tests atall concentrations with highest values of 0.04586 mm/y and 0.234 mm/y in comparison tomartensitic steel with corrosion rates of 0.827 mm/y and 19.84 mm/y at 6 M HCl concen-tration. Micrographs from SEM and EDS analyses showed a less corroded morphology forS32101 steel with fewer pits and slight depletion in the percentage composition of chromiumand other alloying elements.

Item Type: Article
Uncontrolled Keywords: CorrosionDuplexMartensiticHydrochloricStee
Subjects: T Technology > TJ Mechanical engineering and machinery
T Technology > TP Chemical technology
Divisions: Faculty of Engineering, Science and Mathematics > School of Engineering Sciences
Depositing User: Mrs Patricia Nwokealisi
Date Deposited: 31 Dec 2017 16:31
Last Modified: 31 Dec 2017 16:31
URI: http://eprints.covenantuniversity.edu.ng/id/eprint/9899

Actions (login required)

View Item View Item