<> "The repository administrator has not yet configured an RDF license."^^ . <> . . . "ZnO as corrosion inhibitor for dissolution of zinc electrodeposited mild steel in varying HCl concentration"^^ . "The corrosion behavior of Zn electrodeposition on mild steel in varying 0.1 to 0.5 M of HCl with and\r\nwithout inhibitor was studied using weight loss measurement and optical microscope. The (OP) results\r\nrevealed that the corrosion mechanism layers of the zinc plated mild steel without inhibitor has high\r\ncontent corrosivity related to the appearance of cracks due to the dissolution into the acidic medium.\r\nHowever, the zinc electrodeposition with ZnO as an inhibitor in the test medium shows a stable layer\r\nformation. The Zn coatings were found to contain an insoluble corrosion products, which act as a\r\ncorrosion barrier that prevent corrosion from been attacked by the hydrogen presence."^^ . "2011-05-18" . . "6" . "10" . . "International Journal of the Physical Sciences"^^ . . . "19921950" . . . . . . . . . . "O. S. I"^^ . "Fayomi"^^ . "O. S. I Fayomi"^^ . . "A. P. I."^^ . "Popoola"^^ . "A. P. I. Popoola"^^ . . . . . . "ZnO as corrosion inhibitor for dissolution of zinc electrodeposited mild steel in varying HCl concentration (PDF)"^^ . . . "document.pdf"^^ . . . "ZnO as corrosion inhibitor for dissolution of zinc electrodeposited mild steel in varying HCl concentration (Other)"^^ . . . . . . "indexcodes.txt"^^ . . "HTML Summary of #10546 \n\nZnO as corrosion inhibitor for dissolution of zinc electrodeposited mild steel in varying HCl concentration\n\n" . "text/html" . . . "T Technology (General)"@en . . . "TJ Mechanical engineering and machinery"@en . . . . . . . . . "O. S. I"^^ . "Fayomi"^^ . "O. S. I Fayomi"^^ . ""^^ . . "A. P. I."^^ . "Popoola"^^ . "A. P. I. Popoola"^^ . ""^^ .