Afolalu, Sunday A. and Asonaminasom, Ezekiel H and Ongbali, Samson O. and Abioye, Abiodun A. and Udo, Mfon .O and Salawu, Enesi Y. (2018) Dataset on experimental investigation of optimum carburizing temperature and holdingtime of bi-nano additives treatment of AISI 5130 steel. Data in Brief, 19. pp. 2279-2283.
![[img]](http://eprints.covenantuniversity.edu.ng/style/images/fileicons/other.png) |
PDF
Download (117Kb) |
Abstract
Investigation of optimum carburizing temperature and holding time on bi-nano additives treatment of AISI 5130 steel was presented in this study. AISI 5130 steel of 100 kg mass of 0.35% carbon content was buried in pulverized additives consisting of palm kernel and coconut shell using egg shell as an energizer. Four sets of 150�150�150mm3 steel boxes packed with additives mixed at varying weight ratio of 50:30:20 and sixty-four pieces of 20�20�5mm3 AISI 5130 steel were case hardened using muffle furnace (2500 °C maxcapacity) at respective temperatures and time of 950,1000,1050,1100 °C and 60,90,120,180 min. The core, interface and surface hardness of the treated samples with their respective weight loss, wear volume and rate were investigated. This data set could be used in nano-composite match mixed ratio and optimization of carburizing medium and time for any industrial used case hardened steel.
| Item Type: | Article |
|---|---|
| Uncontrolled Keywords: | Bi-nano additive AISI 5130steel Carburizing temperature Time Optimum |
| Subjects: | T Technology > T Technology (General) T Technology > TJ Mechanical engineering and machinery |
| Divisions: | Faculty of Engineering, Science and Mathematics > School of Engineering Sciences |
| Depositing User: | Mrs Hannah Akinwumi |
| Date Deposited: | 24 Jul 2018 13:16 |
| Last Modified: | 24 Jul 2018 13:16 |
| URI: | http://eprints.covenantuniversity.edu.ng/id/eprint/11215 |
Actions (login required)
 |
View Item |