Effect of Cac03 and Wood Flour Filler on the Compression Strength of Coconut (Coir) Fibre Reinforced Polymer (FRP) Composite

Inegbenebor, A.O. and Ogbevire, A. D. and Inegbenebor, A. I. (2007) Effect of Cac03 and Wood Flour Filler on the Compression Strength of Coconut (Coir) Fibre Reinforced Polymer (FRP) Composite. Advanced Materials Research, 18. pp. 249-251.

[img] PDF
Download (381kB)

Abstract

Compression test specimens were produced from the composite material of fibre reinforced polymer (FRP). These specimens were tested on the compressive testing machine. The results obtained showed that 5% coconut fibre volume fraction with 95% volume fraction of polypropylene matrix gave compressive strength value of 39.3 Mpa However, it was observed that when 15% volume fraction of CaC03 and wood flour filler each were added, the compressive strength increased from 39.3 Mpa to 53.3 Mpa and 39.3Mpa to 43.7Mpa respectively. This observation was discussed in respect of the two fillers.

Item Type: Article
Uncontrolled Keywords: Coconut (Coir) fibre, polymer, CaC03, woodflour, filler
Subjects: Q Science > Q Science (General)
Q Science > QD Chemistry
Divisions: Faculty of Engineering, Science and Mathematics > School of Chemistry
Depositing User: Mrs Hannah Akinwumi
Date Deposited: 01 Apr 2015 13:54
Last Modified: 01 Apr 2015 13:54
URI: http://eprints.covenantuniversity.edu.ng/id/eprint/4545

Actions (login required)

View Item View Item