Loto, R. T. and Loto, C. A. and Popoola, A. P. I. (2014) Electrochemical Studies of the corrosion inhibition effect of 2-amino-5-ethyl-1,3,4-thiadiazole on low carbon steel in dilute sulphuric acid. J.Chem.Soc.Pak, 36 (6). pp. 1043-1051.
![[img]](http://eprints.covenantuniversity.edu.ng/style/images/fileicons/application_pdf.png) |
PDF
Download (1MB) |
Abstract
The electrochemical behaviour of carbon steel in 0.5 M H2SO4 was studied in the presence of 2-amino-5-ethyl-1 3 4-thiadiazole (TTD) as inhibitor with the aid of weight loss method, potentiodynamic polarization and open circuit potential measurement technique. The effect of inhibitor concentrations, exposure time, corrosion rate and surface coverage on inhibition efficiency was investigated. Results showed that TTD performed excellently in the acid solution with the inhibition efficiency increasing with increase in inhibitor concentration up to a peak value of 80.67% and 90.5% at maximum concentration from weight loss test and potentiodynamic polarization tests. The compound showed cathodic inhibition tendency in solution with the inhibitor molecules been effectively adsorbed onto the steel surface, stifling the electrochemical reactions responsible for corrosion through the exposure hours. Results from statistical analysis through ANOVA software depicts the overwhelming influence of inhibitor concentration on inhibition efficiency compared to exposure time.
| Item Type: | Article |
|---|---|
| Uncontrolled Keywords: | Corrosion; Thiadiazole; Sulphuric acid; Inhibition and Steel |
| Subjects: | T Technology > T Technology (General) T Technology > TJ Mechanical engineering and machinery |
| Divisions: | Faculty of Engineering, Science and Mathematics > School of Engineering Sciences |
| Depositing User: | Mrs Hannah Akinwumi |
| Date Deposited: | 03 Nov 2016 12:03 |
| Last Modified: | 03 Nov 2016 12:03 |
| URI: | http://eprints.covenantuniversity.edu.ng/id/eprint/7384 |
Actions (login required)
 |
View Item |